Neith Metals is a well-respected manufacturer and supplier located in Cairo, Egypt, with a strong focus on high-performance Tool and Die Steel H13 Bars. These bars are celebrated for their exceptional toughness, heat resistance, and durability, making them perfect for both hot and cold work tooling applications. Thanks to cutting-edge production technology and rigorous quality checks, Neith Metals guarantees that their products consistently meet international standards. The company’s commitment to reliability, precision, and innovation has made it a go-to source for tool steels in demanding industrial settings and precision engineering projects.
Tool and Die Steel H13 Bars are made up of carbon (0.32–0.45%), chromium (4.75–5.50%), molybdenum (1.10–1.75%), vanadium (0.80–1.20%), and silicon (0.80–1.20%). This specific blend creates an ideal mix of toughness, hardness, and resistance to thermal fatigue. Typically, H13 steel achieves a hardness of 48–52 HRC after heat treatment, showcasing excellent hot strength and dimensional stability. It retains its mechanical properties even when subjected to cycles of heating and cooling, making it a great choice for high-temperature working conditions.
| ASTM A681 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| H13 | 0.32 | 0.45 | 0.2 | 0.6 | 0.03 | 0.03 | 0.8 | 1.25 | 4.75 | 5.5 | 0.8 | 1.2 | 1.1 | 1.75 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| 1.2344 /X40CrMoV5-1 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.85 | 1.15 | 1.1 | 1.5 |
| JIS G4404 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| SKD61 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.8 | 1.15 | 1.0 | 1.5 |
| Properties | Metric | Imperial |
| Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) | 1200 – 1590 MPa | 174000 – 231000 psi |
| Tensile strength, yield (@20°C/68°F, varies with heat treatment) | 1000 – 1380 MPa | 145000 – 200000 psi |
| Reduction of area (@20°C/68°F) | 50.00% | 50.00% |
| Modulus of elasticity (@20°C/68°F) | 215 GPa | 31200 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Country | USA | German | Japan |
| Standard | ASTM A681 | DIN EN ISO 4957 | JIS G4404 |
| Grades | H13 | 1.2344/X40CrMoV5-1 | SKD61 |
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 10.4 x 10-6/ºC | 20-100 | – |
| Thermal conductivity | 28.6 W/mK | 215 | – |
When choosing Tool and Die Steel H13 bars, consider factors such as hardness, heat resistance, wear resistance, toughness, machinability, and the specific requirements of the application, including temperature and load conditions.
Tool and Die Steel H13 bars offer limited corrosion resistance due to their high alloy content, but they can still be susceptible to rusting in harsh environments. To improve corrosion resistance, they may require additional surface treatments like coating or regular maintenance to prevent degradation.
Tool and Die Steel H13 Bars find extensive use in creating die-casting dies, hot forging dies, extrusion tools, and plastic molds. Their remarkable resistance to thermal cracking and wear makes them perfect for tools that face high heat and pressure. H13 bars are also utilized in punches, inserts, and shear blades where outstanding toughness and temperature stability are essential. Their versatility has led to widespread adoption in the automotive, aerospace, and heavy engineering sectors for precision tooling and die applications.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Neith Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Alexandria, Egypt
Copyright 2024 Neith Metals. All rights reserved